多晶氧化铝纤维板|洛阳炬星窑炉有限公司

超高温多晶氧化铝纤维板：Ultra-high temperature polycrystalline alumina fiber

该产品系采用多晶氧化铝纤维为主要原料，复配填料和粘合剂等，以吸-压结合的方式成型。与市售煅烧过的纤维制品相比，具有可加工性好、导热系数和容重低的特点。其中FR1800型纤维板和异型制品可满足最高1800℃，长期1750℃的使用要求，已在多座窑炉上替代进口产品使用，节能效果良好，降低了使用成本。

The products are fabricated by suck-press combined method using polycrystalline alumina fiber as main starting materials, adding packing materials and binders. Compared with calcined fiber products, the products are featured with better machinability, lower thermal conductivity and volume weight. The FHB1800 fiber board and special shaped products can long term serve at 1750℃ and at 1800℃ of the maximum, and have been used in many kilns to substitute imported products, saving energy and cutting cost.

产品性能

Product specification

型号参数		GWDL-FR-1000	GWDL-FR-1260	GWDL-FR-1420	GWDL-FR-1500	GWDL-FR-1600	GWDL-FR-1700	GWDL-FR-1800	GWDL-FR-1850
最高使用温度，℃ Max. service temperature		1000	1260	1420	1500	1600	1700	1800	1850
长期使用温度（炉温），℃ Long-term service temperature(furnace temperature)℃		950	1200	1350	1450	1550	1650	1750	1800
制品容重，kg.cm-3 Volume weight		300-600	300-600	400-700	400-700	400-700	400-700	450-700	500-700
导热系数w·(m·K)-1,1200℃ Thermal conductivity		0.14	0.145	0.155	0.15	0.155	0.16	0.17	0.2
加热线收缩率，% Linear shrinkage on heating	1000	≤1	/	/	/	/	/	/	/
	1200	/	≤0.5	≤0.2	/	/	/	/	/
	1400	/	/	≤1	≤0.2	/	/	/	/
	1500	/	/	/	≤1	≤0.2	/	/	/
	1600	/	/	/	/	≤2	≤0.3	/	/
	1700	/	/	/	/	/	≤2	≤0.6	≤0.8
	1800	/	/	/	/	/	/	≤2	≤0.5

应用

Application

高温电炉炉衬、仪器设备加热装置的隔热及电绝缘材料；隧道窑、辊道窑的窑衬材料。

Used as thermal and electric insulating materials for high temperature electric furnace and heating units of equipment, and lining materials for tunnel kiln and roller kiln

产品规格： 标准规格(长 * 宽* 高):900×600×30-100（ mm）,1000×600×30-100（ mm）

Product specification：Standard: 900×600×30-100（ mm）, 1000×600×30-100（ mm）

(Length * width * thickness)

注：产品的技术数据是由所采用的测试标准得的平均值，会在一定的范围内波动，该数据不代表产品的质量保证数据。

【产品名称】多晶氧化铝纤维板

【产品型号】KD-FR

【产品用途】多晶氧化铝纤维板